Manufacturing method of flip-chip structure of iii group semiconductor light emitting device

ABSTRACT

This disclosure refers to a manufacturing method of a flip-chip structure of III group semiconductor light emitting device. The manufacturing method includes steps of: growing a substrate, a buffer layer, an N type nitride semiconductor layer, an active layer and a P type nitride semiconductor layer sequentially from bottom to top to form an epitaxial structure, depositing a transparent conductive layer; defining an isolation groove with the yellow light etching process, depositing a first insulation layer structure, depositing a P type contact metal and N type contact metal, depositing a second insulation layer structure, depositing a flip-chip P type electrode and flip-chip N type electrode, then removing the photo resist by using of the stripping process to get a wafer; thinning, dicing, separating, measuring and sorting the wafer. In this disclosure, structure of the first insulation layer structure which is formed by the Prague reflective layer, the metal layer and the multilayer of oxide insulation, acts as a reflector structure and an insulation layer to replace the flip-chip reflector structure design and the first insulation layer, so that a metal protective layer can be omitted.

FIELD OF THE INVENTION

The disclosure refers to technical field of semiconductor illumination, more particularly to a manufacturing method of a flip-chip structure of III group semiconductor light emitting device.

DESCRIPTION OF THE RELATED ART

Traditionally, a light emitting diode uses normal structure: in which a transparent conductive layer generally uses high penetration rate materials such as ITO and AZO etc. and the electrodes use the materials such as Cr or Pt or Au etc. However, in a flip-chip structure, light activated by active layer emits from the other base of the electrode, thus the requirement of a P type electrode is changed, high reflective material which is used to cover the whole P type nitride semiconductor layer, is used as a reflector. One way to fulfill the requirement is that a P type nitride semiconductor layer is plated by a high penetration transparent electrode with high reflective metal 6, such as ITO or Ag etc. The other way is that P type nitride semiconductor layer is plated by a high reflective metal 6 and used as ohm contact and reflector, such as Ag and Al. No matter which way is selected, metal protective layer 7 (guard metal) must be used on the back of high reflective material to cover high reflective material to avoid instability. The metal protection layer 7, comprises is formed by the steps of: defining a titanium layer and a tungsten layer in sequence or a titanium tungsten alloy layer and then etching with a plurality of holes (vias), structure diagram shown in FIG. 1, covering entire surface of a first insulation layer 8, opening holes to access a N type nitride semiconductor layer and metal protection layer, re-plating a P type contact metal and a N type contact metal, covering a whole second insulation layer, opening holes to access the P type contact metal and the N type contact metal, plating the flip-chip structure P type electrode and N type electrode finally. Due to the high accuracy of the etching holes, complex process is required, and the production cost becomes higher.

SUMMARY OF THE INVENTION

In order to solve the defects existing in the prior art, the disclosure aims to provide a manufacturing method of a flip-chip structure of III group semiconductor light emitting device, which includes steps of:

growing a substrate, a buffer layer, an N type nitride semiconductor layer, an active layer and a P type nitride semiconductor layer sequentially from bottom to top to form an epitaxial structure, wherein the top surface of the epitaxial structure is the top surface of the P type nitride semiconductor layer;

depositing a transparent conductive layer on the top surface of the P type nitride semiconductor, defining a pattern of a linear convex mesa by using of a yellow light etching process, etching the transparent conductive layer, the P type nitride semiconductor layer and the active layer; exposing the N type nitride semiconductor layer; and shrinking the transparent conductive layer with etching solution; finally removing a photo resist to get the linear convex mesa whose top surface has the transparent conductive layer, wherein the linear convex mesa comprises a first top surface, a side surface and a second top surface, the first top surface and the second top surface individually connected with the side surface to form a L shape structure, the first top surface of the linear convex mesa being the top surface of the P type nitride semiconductor layer, the second top surface of the linear convex mesa being the top surface of the N type nitride semiconductor layer; in this step, individually forming the transparent conductive layer and the linear convex mesa, that is, not forming the transparent conductive layer and the linear convex mesa in the same etching step, but forming the transparent conductive layer at first and forming the linear convex mesa on the next, or forming the linear convex mesa at first and forming the transparent conductive layer on the next;

defining an isolation groove with the yellow light etching process, then etching the N type nitride semiconductor layer and the buffer layer to expose the substrate, finally removing the photo resist; or the isolation groove not be arranged in the flip-chip structure of the III group semiconductor light emitting device, or the isolation groove can be arranged in any steps behind this step;

depositing a first insulation layer structure which is formed by a Prague reflective layer, a metal layer and a multilayer of oxide insulation; wherein the Prague reflective layer is deposited at first, then a pattern on the metal layer is defined by a yellow light stripping process, the metal layer is deposited, and the photo resist is removed to get the metal layer by a stripping process, and the multilayer of oxide insulation is deposited, and then a connection pattern between a P type contact metal and the transparent conductive layer and a contact pattern between an N type contact metal and the second top surface of the linear convex mesa by using of the yellow light etching process are defined, then an connecting pattern between the multilayer of the oxide insulation and the Prague reflective layer is continuously etched, and finally the photo resist is removed to get the first insulation layer structure;

defining a pattern of the P type contact metal and a pattern of the N type contact metal by the yellow light etching process, wherein the P type contact metal and the N type contact metal is deposited in the mean time, and then the photo resist is removed with the stripping process to get the P type contact metal and the N type contact metal, therein, a bottom side of the P type contact metal is located on the surface of the transparent conductive layer and the first insulation layer structure, and a bottom side of the N type contact metal is located on the second top surface of the linear convex mesa and the surface of the first insulation layer structure.

depositing the second insulation layer structure, wherein a pattern is defined by the yellow light etching process, the pattern is used for accessing the P type contact metal and the N type contact metal with an opening, then an opening pattern of the second insulation layer structure is etched, and finally the photo resist is removed;

defining a pattern of a flip-chip P type electrode and a flip-chip N type electrode by the yellow light stripping process, wherein the flip-chip P type electrode and the flip-chip N type electrode is deposited, then the photo resist is removed by use of the stripping process to get a wafer; thinning, dicing, separating, measuring and sorting the wafer.

Preferably, the first insulation layer structure is located on the first top surface, the side surface, the second top surface, the transparent conductive layer and the optional isolation groove.

Preferably, the structure of the Prague reflective layer comprises silicon dioxide and titanium dioxide, or silicon dioxide and tantalic oxide, or silicon dioxide and niobium oxide.

Preferably, the thickness of the silicon dioxide is in arrange of 30-1000 nm, the thickness of the titanium dioxide is in arrange of 10-200 nm, the thickness of the tantalic oxide is in a range of 10-200 nm, and the thickness of the niobium oxide is in a range of 10-200 nm.

Preferably, the Prague reflective layer is 3.5 pairs of silicon dioxide/titanium dioxide/silicon dioxide/titanium dioxide/silicon dioxide, or 3.5 pairs of silicon dioxide/tantalic oxide/silicon dioxide/tantalic oxide/silicon dioxide, or 3.5 pairs of silicon dioxide/niobium oxide/silicon dioxide/niobium oxide/silicon dioxide.

Preferably, the first insulation layer structure is formed by the Prague reflective layer, the metal layer, the Prague reflective layer, the metal layer and the multilayer of the oxide insulation, a bottom side of the metal layer is located on the top surface of the Prague reflective layer of the first insulation layer structure, and/or is located in the multilayer of the oxide insulation layer of the first insulation layer structure.

Preferably, the metal layer material comprises at least one of silver, aluminum, silver indium, platinum, nickel and titanium, therein a thickness of the silver, the aluminum, the indium and the platinum is respectively in a range of 50-500 nm, and a thickness of the nickel and the titanium is respectively in a range of 0.3-30 nm

Preferably, the multilayer of the oxide insulation layer is formed by at least two combinations of aluminum oxide, silicon dioxide, titanium dioxide, tantalic oxide, niobium oxide, silicon oxide and silicon nitride, a thickness of each layer of the multilayer of the oxide insulation is in a range of 30-200 nm.

Preferably, the P type contact metal comprises a P type linear electrode and the P type connection metal; the bottom side of the P type linear electrode is located on the surface of the first insulation layer structure and the transparent conductive layer; the bottom side of the P type connection metal is located on the surface of first insulation layer structure; and the N type contact metal comprises an N type linear electrode and the N type connection metal, a bottom side of the N type linear electrode is located on the first insulation layer structure and the second top surface, a bottom side of the N type connection metal is disposed on the surface of the first insulation layer structure.

Preferably, the structure of the P type contact metal and N type contact metal has the same structure which is a single metal layer or a multilayer of metal layer, and both sequentially comprise a first Ni layer, an Al layer, a second Ni layer, an Au layer and a third Ni layer from inner to outer, or sequentially comprise a Ti layer, an Al layer, the second Ni layer, an Au layer and the third Ni layer from inner to outer, or sequentially comprise the Ti layer, the Al layer and the third Ni layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer, the second Ni layer, a Pt layer, the Au layer and the third layer Ni from inner to outer, or sequentially comprise an Cr layer, the Pt layer, the Au layer and the third Ni layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer and the third Ni layer, or sequentially comprise an Rh layer, therein, a thickness of the Rh layer is in a range of 50-3000 nm, a thickness of the first Ni layer is in a range of 0.3-300 nm, a thickness of the Al layer is in a range of 50-300 nm, a thickness of the second Ni layer is in a range of 10-300 nm, a thickness of the Pt layer is in a range of 10-300 nm, a thickness of the Au layer is in a range of 10-3000 nm, a thickness of the third Ni layer is in a range of 0.3-300 nm.

Preferably, the second insulation layer structure is a multilayer of the oxide insulation, the multilayer of the oxide insulation is formed by at least two of the combinations of aluminum oxide, silicon dioxide, titanium dioxide, tantalic oxide, niobium oxide, silicon oxide and silicon nitride, a thickness of each layer of the multilayer of the oxide insulation is in a range of 30-2000 nm.

Preferably, the bottom side of the flip-chip P type electrode is deposited on the surface of the P type contact metal and the second insulation layer, the bottom side of the flip-chip N type electrode is deposited on the surface of the N type contact metal and the second insulation layer structure.

Preferably, the flip-chip P type electrode and the flip-chip N type electrode has the same structure, both sequentially comprise a Ti layer and a second Ni layer and an Au layer from inner to outer, or sequentially comprise a middle Cr layer, a Pt layer, an Au layer, a second Ni layer a Pt layer, a second Ni layer and an AuSn layer from inner to outer, or sequentially comprise a first Ni layer and an Al layer, the second Ni layer and the Au layer from inner to outer, or sequentially comprise the middle Cr layer, the Pt layer and the Au layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer, the middle Cr layer and the second Ni layer and the Au layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer, the second Ni layer, the Pt layer and the Au layer from inner to outer, therein a thickness of the first Ni layer is in a range of 0.4-3 nm, a thickness of the second Ni layer is in a range of 10-300 nm, a thickness of the Ti layer is in a range of 10-300 nm, a thickness of the Al layer is in a range of 50-300 nm, a thickness of the Au layer is in a range of 20-3000 nm, a thickness of the middle Cr layer is in a range of 10-300 nm, a thickness of the Pt layer is in a range of 10-300 nm, and a thickness of the AuSn layer is in a range of 1000-5000 nm.

Compared with the prior art, the manufacturing method of flip-chip structure of III group semiconductor light emitting device in this disclosure, has the following advantages:

The disclosure is provided for using the linear convex mesa to replace a plurality of holes (vias) in the prior art.

In this disclosure, the first insulation layer structure which is formed by the Prague reflective layer, the metal layer and the multilayer of oxide insulation, acts as a reflector structure and an insulation layer to replace the flip-chip reflector structure design and the first insulation layer, and a metal protective layer can be omitted. Furthermore, no reflector structure is provided on the side wall of the traditional flip-chip linear convex mesa without a reflector structure. The reflector structure can be located on the side wall of the linear convex mesa in the disclosure, and an isolation groove can be arranged as well. The isolation groove is also arranged with the reflector structure.

3) In this disclosure, the first step in which the transparent conductive layer and the line convex mesa pattern can be made at the same time, which not only simplifies one process, but also solve the alignment defects between the transparent conductive layer and the linear convex mesa pattern.

(4) In this disclosure, the first insulation layer structure is formed by Prague reflective layer, the metal layer and the multilayer of oxide insulation, and then plated with P type contact metal and N type contact metal. Thus the photoelectric properties of the flip-chip structure can be measured out in this step.

(5) In this disclosure, the transparent conductive layer and the first insulation layer structure of the new structure is arranged sequentially on the first surface of the linear convex mesa. Namely, in this disclosure, “conductive metal layer with high reflectivity of 6” and ITO or P type nitride semiconductor layer is not set in direct contact on the P type nitride semiconductor layer, but the non-conductive first conductive insulation layer structure 8 (specifically Prague reflector) and the transparent conductive layer which is located on top of the P type nitride semiconductor layer is in direct contact. And thus it makes the structure of flip-chip LED chip in this disclosure significantly different from the flip-chip structure shown in FIG. 1.

(6) when the first insulation layer structure of the disclosure is formed by Prague reflective layer, the metal layer and the multilayer of oxide insulation, the first insulation layer is provided with a metal interlayer structure, in particular the metal layer is located between the Prague reflective layer and the multilayer oxide insulation layer, or the metal layer is sandwiched inside the internal layer of the multilayer of oxide insulation. Therefore, in order to obtain a flip-chip LED chip, this disclosure provides a novel insulation layer structure.

Of course, the implementation of the disclosure of any product will not necessarily require all of the mentioned technical results above can be achieved at the same time.

BRIEF DESCRIPTION OF THE ATTACHED DRAWINGS

The attached drawings described here which is provided for further understanding of this disclosure, constitute a part of the disclosure, and the illustrative embodiment is used for the interpretation of this disclosure, the disclosure does not constitute improper limit.

In the drawings:

FIG. 1 is a schematic for the flip-chip structure of III group nitride semiconductor light emitting device in prior art.

FIG. 2A to FIG. 2G are a schematic of making flow of the flip-chip LED chip of which the first insulation layer structure is formed by the Prague reflective layer, the metal layer and the multilayer of oxide insulation.

FIG. 3A to 3B are the top view and cross-section view of the multi vias in prior art respectively.

FIG. 4A to FIG. 4B are the top view and cross-section view of linear convex mesa respectively.

FIG. 5 is the cross-section view of P type linear electrode.

FIG. 6 is the cross-section view of N type linear electrode.

FIG. 7 is another schematic of flip-chip LED chip of which the first insulation layer is formed by Prague reflective layer, metal layer and multi layer of oxide insulation.

FIG. 8 is the diagram of the luminance and current and voltage characteristics of the flip-chip LED chip.

FIG. 9 is the diagram of the current characteristics and the peak wavelength of the flip-chip LED chip.

In the drawings:

-   -   1—Substrate     -   2—Buffer layer     -   3—N type nitride semiconductor layer     -   4—Active layer     -   5—P type nitride semiconductor layer     -   6—Metal layer with high reflectivity     -   7—metal protection layer     -   8-1—the first insulation layer     -   801—single-layer oxide insulation layer     -   802—Metal layer     -   803—Prague reflective layer     -   9—P type contact metal     -   10—N type contact metal     -   11—2 the second insulation layer     -   13—Flip-chip N type electrode     -   14—Transparent conductive layer     -   15—P type linear electrode     -   17—N type linear electrode     -   19—Linear convex mesa     -   19-1—The first top surface     -   19-2—Side surface     -   19-3—The second top surface     -   20—Isolation groove     -   21—P type contact metal     -   22—N type contact metal

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

If certain words are used to refer to a specific component in the specification and claims, the skilled in the field should understand that hardware manufacturers may use different terms to name the same component. This specification and the claim does not differentiate each other in the way of the name, but uses the functional differences of the component as the criteria. As mentioned in the whole specification and claims, the word “contains” is an open language, it should be interpreted as “including but not limited to”. The word “Roughly” refers to the range of error acceptance, the skilled in the field should solve the technical defects within a certain a range of error and achieve the basic technical effect. In addition, the word “coupling” includes any direct and indirect means of electrical coupling. Therefore, if the description “a first coupling device coupled to a second device” is used, it means the first device can be directly connected to the second electrical coupled device, or by indirect means it is electrically coupled to the second device by the other device or coupling. The following instructions are described as preferred embodiment for the implementation of this disclosure. However it is the general principle that the purpose of description of this disclosure is not limited to the scope of disclosure. The scope of protection of this disclosure shall be subject to the requirements defined in the appended claims.

Further details of the disclosure is provided according to the drawings, but it is not regarded as a restriction on the disclosure.

Embodiment 1

This disclosure provides a manufacturing method of the flip-chip structure of III group semiconductor light emitting device, details are shown in FIG. 2A-and FIG. 2G.

The manufacturing method includes the steps of:

a first step, shown in FIG. 2A, including the steps of: growing the Substrate 1, buffer layer 2, N type nitride semiconductor 3, active layer 4 and the P type nitride semiconductor sequentially from bottom to top to form the epitaxial structure, wherein the top surface of the epitaxial structure is the top surface of the P type nitride semiconductor layer 5.

This

a second step, shown in FIG. 2B including the steps of: depositing a transparent conductive layer 14 on the top surface of P type nitride semiconductor 5, defining a pattern of a linear convex mesa by using of the yellow light etching process, etching the transparent conductive layer 14 and the P type nitride semiconductor layer 5 and active layer 4, exposing the N type nitride semiconductor layer 3, and then shrinking the transparent conductive layer 14 with etching solution; finally removing the photo resist to get the linear convex mesa 19, whose top surface has the transparent conductive layer 14 (the transparent conductive layer 14 and the convex mesa 19 can be made individually on this step);

In this disclosure, the transparent conductive layer 14 and the linear convex mesa 19 are formed at the same time, that is, the transparent conductive layer 14 is deposited on the entire surface of the P type nitride semiconductor 5, and the transparent conductive layer 14 and the linear convex surface 19 are formed in one etching step. The transparent conductive layer 14 and the linear convex mesa 19 are formed individually, that is, there are two situations, one is to form transparent conductive layer 14 first, then the linear convex mesa 19. In details, the shape of the transparent conductive layer 14 and the transparent conductive layer 14 is deposited on the P type nitride the semiconductor 5 with the yellow light etching, then the shape of the convex is defined and etched to get the convex mesa 19. The other one is to make the linear convex mesa 19 first, and then the transparent conductive layer 14. That is, the convex shape is firstly defined and etched to get the linear convex surface 19, and the transparent conductive layer 14 is deposited on the first top surface 19-1 of the convex mesa with the yellow light.

A third step as shown in FIG. 2C including the steps of: defining pattern of the isolation groove 20 with yellow light etching process, then etching the N type semiconductor layer 3 and buffer layer 2 to expose the substrate 1, finally removing the photo resist. This step can be arranged in any step.

In this disclosure, the isolation groove 20 of the LED chip is correspondingly provided with any one of the following conditions:

not set the isolation groove (such as eutectic solder);

only contains the second insulation layer 11-1 above the isolation groove;

a first insulation layer 8-1 and a second insulation layer 11-1 exists above the isolation groove

the isolation groove above only contains the first insulation layer 8-1.

As mentioned above, the LED chip can be provided with the isolation groove 20, and also can not contain the isolation groove 20, and the isolation groove 20 is generally formed before the second insulation layer structure formed. In details, the isolation groove is formed before the first insulation layer structure 8-1 formed, and the isolation groove comprises a first insulation layer 8-1 and a second insulation layer 11-1, or it only comprises the first insulation layer 8-1. the isolation groove can also be formed in any of the steps before the second insulation layer 11-1 or after the first insulation layer structure 8-1, so that the isolation groove only comprises the second insulation layer 11-1.

A fourth step as shown in FIG. 2D including the steps of: the first insulation layer structure 8-1 is formed by a Prague reflective layer, a metal layer and a multilayer of oxide insulation. In this step, the Prague reflective layer is deposited at first, then a pattern on the metal layer is defined by a yellow light stripping process, the metal layer is deposited, and the photo resist is removed to get metal layer by a stripping process, then the multilayer of oxide insulation is deposited, then a connection pattern between P type contact metal and transparent conductive layer of an N type contact metal 10 and the second top surface 19-3 of the linear convex mesa by using of the yellow light etching process are defined, then an connecting pattern between the multilayer of the oxide insulation and the Prague reflective layer is continuously etched, and finally the photo resist is removed to get the first insulation layer structure 8-1. The connection pattern can be dotted, linear or flat surface, this is not restricted in the disclosure.

As shown in the drawings, the first insulation layer structure 8-1 is formed by the Prague reflective layer, the metal layer and the single layer of oxide insulation or multilayer of oxide insulation. However, the first insulation layer structure 8-1 which is formed by the Prague reflective layer 803, the metal layer 802 and the multilayer of oxide insulation 804 has better effect than what formed by the Prague reflective layer 803, the metal layer 802 and the single layer oxide insulation 801. Hence only the optimized scheme is protected in this disclosure.

A fifth step as shown in FIG. 2E including the steps of: defining a pattern of the P type contact metal 9 and a pattern of the N type contact metal 10 by the yellow light etching process, and depositing the P type contact metal 9 and the N type contact metal 10 in the mean time, and then the photo resist is removed with the stripping process to get the P type contact metal 9 and the N type contact metal 10;

As shown in FIG. 2E, the P type contact metal and the N type contact metal comprises a P type linear electrode 15, an N type linear electrode 17, a P type connection metal 21 and an N type connection metal 22. The bottom end of P type linear electrode 15 is located on the surface of the first insulation layer structure 8-1 and a transparent conductive layer 14, the bottom end of the N type linear electrode 17 is located on the surface of the first insulation layer structure 8-1 and the second top surface of the linear convex mesa 19-3, the bottom end of the N type connection metal 22 is located on the surface of the first insulation layer structure 8-1;

In fact, the structure of the P type contact metal 9 and the N type contact metal 10 can be selected from the following three types alternately:

The P type contact metal 9 comprises the metal on the entire surface, the bottom end of the entire surface of the metal is located on the surface of the first insulation layer structure 8-1 and the transparent conductive layer 14, and the exposed transparent conductive layer 14 is completely covered by the lower end of the metal of the entire surface;

The N type contact metal 10 is comprises the metal on the entire surface, the bottom end of the entire surface of the metal is located on the surface of the first insulation layer structure 8-1 and the second top surface 19-3 of the linear convex mesa, and the exposed top surface 19-3 is completely covered by the metal of the entire surface;

(2) the P type contact metal 9 comprises the P type linear electrode 15 and a normal P type pad. The bottom end of the normal P type pad is located on the surface of the first insulation layer 8-1, the bottom end of the P type linear electrode 15 is located on the transparent conductive layer 6 or on the surface of the first insulation layer structure 8-1 and the transparent conductive layer 6

The N type contact metal 10 comprises the N type linear electrode 17 and a normal N type pad, the bottom end of the normal N type pad is located on the surface of the first insulation layer 8-1, the bottom end of the N type linear electrode 17 is located on the second top surface 19-3 of the linear convex mesa or on the second top surface of the first insulation layer structure 8-1 and linear convex mesa.

(3) The P type contact metal 9 comprises the P type linear electrode 15 and the P contact metal 21, the bottom end of the P type linear electrode 15 is located on the transparent conductive layer 6 or on the surface of the first insulation layer 8-1 and transparent conductive layer 6, the bottom end of the P type contact metal 21 is located on the surface of the first insulation layer structure 8-1

The N type contact metal 10 comprises the N type linear electrode 17 and the N type connection metal 22, the bottom end of the N type linear electrode 17 is located on the second top surface 19-3 of the linear convex mesa or on the first insulation layer 8-1 and the second top surface 19-3 of the first insulation layer, the bottom end of the N type connection metal 22 is located on the surface of the first insulation layer structure 8-1.

As the skilled in the field known, the main difference between the pad of the scheme (2) and the connection metal of scheme (3) is in that both the size and the shape of the pad are fixed, while both the size and the shape of the metal connection are not restricted.

In addition, no matter which scheme of the above (1) to (3) the contact metal belongs to, the patterns of the P type contact metal and the N type contact metal re defined by the yellow light stripping process, the P type contact metal and the N type contact metal are deposited by using of electron beam evaporation, and then the photo resist is removed by the stripping process to get the P type contact metal and the N type contact metal.

The sixth step as shown in FIG. 2F including the steps of: depositing the second insulation layer structure 11-1. Wherein a pattern is defined by the yellow light etching process, the pattern is used for accessing the P type contact metal 9 and the N type contact metal 10 with an opening, then an opening pattern of the second insulation layer structure 11-1 is etched, and finally the photo resist is removed.

Similarly, the pattern of opening and access can be shaped into linear, dotted or flat. This is not restricted in the disclosure.

The second insulation layer is a single layer oxide insulation or a multilayer of oxide insulation. As known by the skilled in the field, no matter which of these three structures of the P type contact metal 9 and the N type contact metal 10 belongs to, the second insulation layer structure 11-1 can be a single layer or a multilayer of oxide insulation.

A seventh step as shown as FIG. 2G including the steps of: defining a pattern of a flip-chip P type electrode 12 and a flip-chip N type electrode 13 by the yellow light stripping process, wherein the flip-chip P type electrode 13 and the flip-chip N type electrode 13 is deposited, then the photo resist is removed

An eighth step including the steps of: thinning, dicing, separating, measuring and sorting the wafer. This step is obtained through the production process of the prior art.

By the use of the method above, the flip-chip structure of III group semiconductor light emitting device is attained. The flip-chip structure includes the substrate 1, a buffer layer 2, the N type nitride semiconductor layer 3, the active layer 4, the P type nitride semiconductor layer 5, the first insulation layer structure 8-1, the P type contact metal 9, the N type contact metal 10, the second insulation layer structure 11-1, the flip-chip P type electrode 12, the flip-chip N type electrode 13 and the transparent conductive layer 14.

The substrate 1, the buffer layer 2, the N nitride semiconductor layer 3, the active layer 4, and the P nitride semiconductor layer 5 are formed into a nitride semiconductor structure with linear convex mesa 19.

The linear convex mesa 19 comprises the first top surface 19-1 of linear convex mesa, the side surface 19-2 and the second top surface 19-3 of the linear convex mesa. An L shape is formed by the side surface 19-2 and the second top surface 19-3 located on the both ends of the first top surface 19-1.

The first top surface 19-1 of the convex mesa is the top surface of the P type nitride semiconductor layer 5, it becomes a top surface of the linear convex mesa. The second top surface 19-3 of the convex mesa is the top surface of the N type nitride semiconductor layer, and it becomes a bottom surface of the linear convex mesa. The side surface 19-2 is connected between the first top surface 19-1 and the second top surface 19-3, and the convex mesa comprises these three one.

The etched area of linear convex mesa 19 is a single or multiline, that is, the linear convex mesa 19 is referred to the convex mesa formed by the etching of planar cross-cutting.

The first top surface 19-1 of the linear convex mesa is disposed with the transparent conductive layer 14

Material of the transparent conductive layer 14 can be at least one of Indium tin oxide (ITO), Cadmium tin oxide, Zinc oxide, Indium oxide, Tin oxide, Copper (II) Aluminum oxide, Copper (II) Gallium (III) oxide and Strontium Copper oxide.

The first insulation layer structure 8-1 is located on all the first top surface 19-1, the side surface 19-2 and the second top surface 19-3 and the transparent conductive layer 14 of the convex mesa.

Preferably, the first insulation layer structure 8-1 is formed by the Prague reflective layer, the metal layer and the multilayer of oxide insulation.

The Prague reflective layer structure comprises silicon dioxide and titanium dioxide, or is comprising of silicon dioxide and tantalic oxide, or is comprising of silicon dioxide and niobium oxide. In the Prague reflective layer, the thickness of the silicon dioxide is in a range of 30-1000 nm, the thickness of the titanium dioxide is in a range of 10-200 nm, the thickness of the tantalic oxide is in a range of 10-200 nm, and the thickness of the niobium oxide is in a range of 10-200 nm.

Preferably, the Prague reflective layer is 3.5 pairs of silicon dioxide/titanium dioxide/silicon dioxide/titanium dioxide/silicon dioxide, or 3.5 pairs of silicon dioxide/tantalic oxide/silicon dioxide/tantalic oxide/silicon dioxide, or 3.5 pairs of silicon dioxide/niobium oxide/silicon dioxide/niobium oxide/silicon dioxide.

Preferably, the first insulation layer structure 8-1 is formed by the Prague reflective layer, the metal layer, the Prague reflective layer, the metal layer and the multilayer of the oxide insulation, a bottom side of the metal layer is located on the top surface of the Prague reflective layer of the first insulation layer structure 8-1, and/or is located in the multilayer of the oxide insulation layer of the first insulation layer structure 8-1. No direct contact is allowed by such a setting between the metal layer and the transparent conductive layer 14, hence insulation is guaranteed on the first insulation layer structure 18-1 of the metal layer 802.

The metal layer material comprises at least one of silver, aluminum, silver indium, platinum, nickel and titanium, therein a thickness of the silver, the aluminum, the indium and the platinum is respectively in a range of 50-500 nm, and a thickness of the nickel and the titanium is respectively in a range of 0.3-30 nm.

The multilayer of the oxide insulation layer is formed by at least two combinations of aluminum oxide, silicon dioxide, titanium dioxide, tantalic oxide, niobium oxide, silicon oxide and silicon nitride.

A thickness of each layer of the multilayer of the oxide insulation is in a range of 30-200 nm.

The bottom end of the P type linear electrode is located on the surface 8-1 of the first insulation layer structure and the transparent conductive layer 14,

The bottom end of the N type linear electrode 10 is located on the surface of the first insulation layer structure 8-1 and the second surface 19-3 of linear convex mesa,

The P type contact metal 9 comprises a P type linear electrode 15 and the P type connection metal 21. The bottom end of the P type linear electrode 15 is located on the surface of the first insulation layer structure 18-1 and the transparent conductive layer 14, and the bottom end of the P type contact metal 21 is located on the surface of the first insulation layer structure 8-1.

The N type contact metal 10 comprises an N type linear electrode 17 and the N type connection metal 22. The bottom end of the N type linear electrode 17 is located on the first insulation layer structure 8-1 and the second top surface 19-3 of the linear convex mesa, the bottom end of the N type connection metal is located on the surface of the first insulation layer structure 8-1.

The structure of the P type contact metal 9 and the N type contact metal 10 is a single metal layer or a multilayer metal layer

The P type contact metal 9 and the N type contact metal 10 have the same structure

The P type contact metal 9 and the N type contact metal 10 sequentially comprise a first Ni layer, an Al layer, a second Ni layer, an Au layer and a third Ni layer from inner to outer, or sequentially comprise a Ti layer, an Al layer, the second Ni layer, an Au layer and the third Ni layer from inner to outer, or sequentially comprise the Ti layer, the Al layer and the third Ni layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer, the second Ni layer, a Pt layer, the Au layer and the third layer Ni from inner to outer, or sequentially comprise an Cr layer, the Pt layer, the Au layer and the third Ni layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer and the third Ni layer, or sequentially comprise an Rh layer, therein, a thickness of the Rh layer is in a range of 50-3000 nm, a thickness of the first Ni layer is in a range of 0.3-300 nm, a thickness of the Al layer is in a range of 50-300 nm, a thickness of the second Ni layer is in a range of 10-300 nm, a thickness of the Pt layer is in a range of 10-300 nm, a thickness of the Au layer is in a range of 10-3000 nm, a thickness of the third Ni layer is in a range of 0.3-300 nm.

The top surface of the first insulation layer 8-1 and the P type contact metal 9 and N type contact metal 10 comprise the second insulation layer 11-1

The second insulation layer 11-1 is multilayer oxide insulation,

The multilayer of the oxide insulation is formed by at least two of the combinations of aluminum oxide, silicon dioxide, titanium dioxide, tantalic oxide, niobium oxide, silicon oxide and silicon nitride.

A thickness of each layer of the multilayer oxide insulation layer is 30-2000 nm

The bottom side of the flip-chip P type electrode 12 is disposed on the surface of the P type contact metal 9 and the second insulation layer 11-1

The bottom side of the flip-chip N type electrode is disposed on the surface of the N type contact metal and the second insulation layer structure 1-1.

The flip-chip P type electrode 12 and the flip-chip N type electrode 13 have the same structure. The flip-chip P type electrode 12 and the flip-chip N type electrode 13 sequentially comprises a Ti layer and a second Ni layer and an Au layer from inner to outer, or sequentially comprise a middle Cr layer, a Pt layer, an Au layer, a second Ni layer a Pt layer, a second Ni layer and an AuSn layer from inner to outer, or sequentially comprise a first Ni layer and an Al layer, the second Ni layer and the Au layer from inner to outer, or sequentially comprise the middle Cr layer, the Pt layer and the Au layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer, the middle Cr layer and the second Ni layer and the Au layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer, the second Ni layer, the Pt layer and the Au layer from inner to outer, therein a thickness of the first Ni layer is in a range of 0.4-3 nm, a thickness of the second Ni layer is in a range of 10-300 nm, a thickness of the Ti layer is in a range of 10-300 nm, a thickness of the Al layer is in a range of 50-300 nm, a thickness of the Au layer is in a range of 20-3000 nm, a thickness of the middle Cr layer is in a range of 10-300 nm, a thickness of the Pt layer is in a range of 10-300 nm, and a thickness of the AuSn layer is in a range of 1000-5000 nm.

Embodiment 2

The novel structure of this disclosure is provided for using the linear convex mesa technique to replace a plurality of holes (vias)

As shown in FIG. 3a is the top view of a plurality of vias in the prior art, FIG. 3B is the sectional view of FIG. 3A cut along the A-B direction

FIG. 4A is the top view of linear convex mesa, FIG. 4B is the sectional view of FIG. 4A cut along A-B

The area etched out from convex mesa 19 is a single or multiline

The nitride semiconductor structure with the convex mesa 19 includes the substrate 1, the buffer layer 2, the N type nitride semiconductor 3, the active layer 4 and the P type nitride semiconductor layer 5.

The linear convex mesa comprises the first top surface 19-1 and the side surface 19-2 and the second top surface 19-3. An L shape is formed by the side surface 19-2 and the second top surface 19-3 located on the both ends of the first top surface 19-1.

The first top surface 19-1 of the convex mesa is the top surface of the P type nitride semiconductor layer, and the second top surface 19-3 of the convex mesa is the top surface of the N type nitride semiconductor layer.

Embodiment 3

The bottom end of the P type linear electrode 15 is located on the surface of the first insulation layer structure 8-1 and the transparent conductive layer 14 (as shown in FIG. 5).

Embodiment 4

The groove covering the entire linear convex mesa of the N type linear electrode 17 is located on the first insulation layer 8-1 and the second surface 19-3 (as shown in FIG. 6).

Embodiment 5

In the fourth step, as shown in FIG. 2D (or FIG. 7), the first insulation layer structure 8-1 is formed by the Prague reflective layer-metal layer-multilayer insulation layer in this disclosure.

The Prague reflective layer structure comprises silicon dioxide (SiO₂) and titanium dioxide (TiO₂), or silicon dioxide (SiO₂) and tantalic oxide (Ta₂O₅), or silicon dioxide (SiO₂) and niobium oxide (Nb₂O₅). The thickness of silicon (SiO₂) is in a range of 30-1000 nm, the thickness of the titanium dioxide (TiO₂) is in a range of 10-200 nm, the thickness of the tantalic dioxide tantalic oxide (Ta₂O₅) is in a range of 10-200 nm, the thickness of the niobium oxide (Nb₂O₅) is in a range of 10-200 nm.

Wherein, “metal layer 802” is not included in the first insulation layer 8-1 of the side surface 19-2 in FIG. 7, but it is included in the first insulation layer 8-1 of the side surface 19-2 in FIG. 2d . That is, the side surface 19-2 of the first insulation layer 8-1 can be “the Prague reflective layer and the oxide insulation layer”, but the one of the transparent conductive layer 14 is “the Prague reflective layer, the metal layer and multilayer of oxide insulation”

In the preferred scheme above, the Prague reflective layer is 3.5 pairs of silicon dioxide/titanium dioxide/silicon dioxide/titanium dioxide/silicon dioxide, or 3.5 pairs of silicon dioxide/tantalic oxide/silicon dioxide/tantalic oxide/silicon dioxide, or 3.5 pairs of silicon dioxide/niobium oxide/silicon dioxide/niobium oxide/silicon dioxide.

Of the scheme above, the first insulation layer structure 8-1 is formed by the Prague reflective layer, the metal layer, the Prague reflective layer, the metal layer and the multilayer of oxide insulation.

The bottom end of the metal layer is located on top surface of the Prague reflective layer of the first insulation layer structure 8-1 and inside the multi layer of oxide insulation of the first insulation layer structure 8-1.

The multilayer of oxide insulation comprises at least one combination of aluminum oxide (Al₂O₃), silicon dioxide (SiO₂), titanium dioxide (TiO₂), tantalic oxide (Ta₂O₅), niobium oxide (Nb₂O₅), silicon oxide (Si₂N₂O) and silicon nitride (Si₃N₄). A thickness of each layer of the multilayer of the oxide insulation is in a range of 30-200 nm.

The material of multilayer oxide insulation layer is comprising of at least one combination of aluminum oxide (Al₂O₃), silicon dioxide (SiO₂), titanium dioxide (TiO₂), tantalic oxide (Ta₂O₅), niobium oxide (Nb₂O₅), silicon oxide (Si₂N₂O) and silicon nitride (Si₃N₄), wherein each layer thickness of the multilayer oxide insulation layer is in a range of 30-2000 nm

The multilayer of oxide insulation above is the combination of silicon dioxide (SiO₂) and titanium dioxide (TiO₂) wherein each layer thickness is in a range of 30-2000 nm.

Of the scheme above, the first insulation layer structure 8-1 is formed by the Prague reflective layer, the metal layer, the Prague reflective layer, the metal layer and the multilayer of oxide insulation, the method is: the Prague reflective layer is deposited at first, then a pattern on the metal layer is defined by a yellow light stripping process, the metal layer is deposited, and the photo resist is removed to get the metal layer by a stripping process, and the multilayer of oxide insulation is deposited, and then a connection pattern between a P type contact metal 9 and the transparent conductive layer 14 and a contact pattern between an N type contact metal 10 and the second top surface of the linear convex mesa 19-3 by using of the yellow light etching process are defined, then an connecting pattern between the multilayer of the oxide insulation and the Prague reflective layer is continuously etched, and finally the photo resist is removed to get the first insulation layer structure 8-1;

Embodiment 6

On the fifth step of the chip making, structure diagram is shown as FIG. 2E, the method is: defining a pattern of the P type contact metal 9 and a pattern of the N type contact metal 10 by the yellow light etching process, wherein the P type contact metal 9 and the N type contact metal 10 is deposited in the mean time, and then the photo resist is removed with the stripping process to get the P type contact metal 9 and the N type contact metal 10.

As shown in FIG. 2E, the P type contact metal 9 and N type contact metal 10 is P/N type linear electrode 15&17 and P/N type contact metal 21 &22; the bottom end of P type linear electrode 15 is located on the surface of the first insulation layer 8-1 and the second top surface 19-3 of the linear convex mesa, the bottom end of the P/N type connection metal 21 &22 is located on the surface of the first insulation layer 8-1.

Embodiment 7

On the sixth step of the chip making, the second insulation layer 11-1 of this disclosure is multilayer of oxide insulation.

All the top surface of the first insulation layer 8-1 and the P type contact metal 9 and the N type contact metal 10 comprise a second insulation layer 11-1.

The material of the multilayer of oxide insulation is the several combinations of aluminum oxide (Al₂O₃), silicon dioxide (SiO₂), titanium dioxide (TiO₂), tantalic oxide (Ta₂O₅), niobium oxide (Nb₂O₅), silicon oxide (Si₂N₂O) and silicon nitride, (Si₃N₄).

Each layer thickness of the multilayer of oxide insulation is in a range of 30-2000 nm in prior art.

Material structure of the preferable multilayer of oxide insulation is the combination of silicon dioxide (SiO₂) and titanium dioxide (TiO₂), the thickness of the titanium dioxide is in a range of 10-300 nm, the thickness of the silicon dioxide is in a range of 100-1000 nm.

Embodiment 8

Based on the Embodiment 1, Embodiment 2, Embodiment 3, Embodiment 4 and Embodiment 5, the flip-chip light emitting device is made with the specification—840 um×410 um. The manufacturing method for a flip-chip light emitting device of III group nitride semiconductor includes the following steps:

The first step: structure diagram shown as FIG. 2A, the method is growing the substrate 1, the buffer layer 2, the N type nitride semiconductor 3, the active layer 4 and the P type nitride semiconductor 5 sequentially from bottom to top to form an epitaxial structure, wherein the top surface of the epitaxial structure is the top surface of the P type nitride semiconductor layer 5, the epitaxial structure is attained from the manufacturing process of prior art.

The second step: structure diagram shown as FIG. 2B, by way of electron beam evaporation or sputtering, or reactive plasma deposition (reactive plasma, deposition, RPD), depositing ITO (indium tin oxide) to form the transparent conductive layer 14 on the surface of the P type nitride semiconductor 5, wherein the ITO thickness is 10-400 nm, then defining a pattern of a linear convex mesa 19 by using of the yellow light etching process, then etching with ICP on the transparent conductive layer 14 and the P type nitride semiconductor layer 5 and active layer 4, exposing N type nitride semiconductor layer 3, and shrinking the transparent conductive layer 14 with the etching solution, finally removing the photo resist to get the linear convex mesa 19 whose the top surface has transparent conductive layer 14 (the transparent conductive layer 14 and the linear convex mesa 9 can be done individually); then annealing Wafer on high temperature to make sure the good ohm Contact and penetration rate is formed between transparent conductive layer 14 and the P type nitride semiconductor layer 5. Annealing method: using fast annealing furnace (RTA) for fast annealing, the temperature is 560 degrees Celsius, the timeslot is 3 minutes.

The third step: structure diagram shown as FIG. 2C, a method: defining the pattern of isolation groove 20 with the yellow light etching process, then etching the N type nitride semiconductor layer 3 and the buffer layer 2 to expose the substrate 1, finally removing the photo resist. This step can be located in any steps behind this step.

The forth step: the structure of the first insulation layer 8-1 is formed by the Prague reflective layer, the metal layer and the multilayer of oxide insulation, structure diagram shown in FIG. 2D, the Prague reflective layer is deposited with optical vacuum coating machine, then metal layer pattern is defined with yellow light stripping process, metal layer is deposited with electron beam evaporation, and the photo resist is removed by the stripping process to get the metal layer, then the multilayer of oxide insulation is plated with optical vacuum coating machine, then the connection pattern between the P type contact metal and transparent conductive layer 14, and the connection pattern of N type contact metal and the second top surface 19-3 of the linear convex mesa are defined by using of the yellow light etching process, then the connecting pattern of multilayer of oxide insulation and Prague reflective layer is continuously etched, finally the photo resist is removed to get the first insulation layer structure.

In this embodiment, the structure of the Prague reflective layer is SiO2/TiO2/SiO2/TiO2/SiO2/TiO2/SiO2, wherein the thickness of the SiO2 is in a range of 30-1000 nm, and the thickness of the TiO2 is in a range of 10-200 nm

In this embodiment, the structure of the metal layer comprises aluminum and titanium, the thickness of aluminum titanium is in a range of 50-500 nm, the thickness of titanium is in a range of 0.3-30 nm.

In this embodiment, the structure of the multilayer of oxide insulation comprises titanium dioxide (TiO2) and silicon dioxide (SiO2), wherein the thickness of each layer is in a range of 30-2000 nm.

The fifth step: structure diagram shown as FIG. 2E, method including: defining the pattern of the P type contact metal 9 and the N type contact metal 10 by the yellow light stripping process (including P/N type contact metal 10 and P/N connection metal 21, 22), and depositing P type contact metal 9 and N type contact metal 10 in the mean time, then removing the photo resist is removed with the stripping process to get the P type contact metal 9 and N type contact metal 10.

In this embodiment, P type contact metal 9 and N type contact metal 10 has the same structure, and both sequentially comprise with the first Ni layer, Al layer, Ni layer, the second Au layer and the third Ni layer from inner to outer, wherein the thickness of the first Ni layer is in a range of 0.4-3 nm, the thickness of the Al layer is in a range of 50-300 nm layer, the thickness of the second Ni layer is in a range of 10-300 nm, the thickness of the Au layer is in a range of 10-3000 nm, the thickness of the third Ni layer in a range of is 0.4-3 nm.

The sixth step: the structure of the second insulation layer 11-1 is multilayer of oxide insulation, structure diagram shown as FIG. 2F, depositing the multilayer of oxide insulation by using of optical vacuum coating machine, the multilayer of oxide insulation is the combination of Titanium dioxide (TiO₂) and Silicon dioxide (SiO₂), wherein the thickness of Titanium dioxide (TiO₂) is in a range of 10-300 nm and the thickness of silicon dioxide (SiO₂) is in a range of 10-1000 nm.

The seventh step: structure diagram shown as FIG. 2G, method including: defining the pattern of flip-chip P/N type electrode 12&13 with the yellow light stripping process, depositing flip-chip P/N type electrode 12&13 with electron beam evaporation in the mean time, then removing the photo resist with the stripping process.

In this embodiment, flip-chip P type electrode 12 and flip-chip N type electrode 13 has the same structure, and both sequentially comprise with the first Ti layer, the second Ni layer, the Au layer from inner to outer, or sequentially comprise with the first Ni layer, Al layer, the second Ni layer, Au layer from inner to outer, wherein the thickness of the Ti layer is in a range of 10-300 nm, the thickness of the first Ni layer is in a range of 0.4-3 nm, the thickness of the second Ni layer is in a range of 10-300 nm, the thickness of the Au layer is in a range of 20-3000 nm.

The eighth step: the wafer is thinned, diced, separated, tested and sorted, the steps are obtained through the production process of the prior art

The ninth step: packing the flip chip package and measuring the photoelectric characteristic

The characteristics of the test results is shown as FIG. 8 and FIG. 9 for the product which is made according to method of the embodiment 8

As shown in FIG. 8 and FIG. 9, the photoelectric properties of the product can be found: when input current is 50 mA and the voltage is 2.88V, then the product brightness is 55.3 lm (color 6900K) and the peak wavelength is 447.1 nm, when input current is 300 mA and the voltage is 3.01V, then the product brightness is 92.61 lm (color 7174K) and the peak wavelength is 446.2 nm, when input current is 860 mA and the voltage is 3.29V, then the product brightness is 157.4 lm (color 7724K) and the peak wavelength is 447.1 nm; From FIG. 8 and FIG. 9, it is concluded that this product is provided with higher operating current and lower voltage and higher brightness and less wavelength shift, compared with the normal structure product.

Compared with the prior art, the manufacturing method of flip-chip structure of III group semiconductor light emitting device has the advantages in the following:

The method of the disclosure is to replace a plurality of holes (vias) in the prior art by using of the linear convex mesa technique.

In this disclosure, the structure of the first insulation layer which is formed by the Prague reflective layer, the metal layer and the multilayer of oxide insulation, acts as a reflector and an insulation layer to replace the flip-chip reflector and a first insulation layer 8. The metal protective layer 7 can be omitted. And no reflector structure is provided on the side wall of the traditional flip-chip linear convex mesa. Side wall of linear convex mesa in this disclosure is provide with reflector structure and isolation groove, and the isolation groove is also provided with a reflector.

In this disclosure, it is acceptable to make the transparent conductive layer and the line convex mesa pattern together on the first step. It is not only to simplify one process, but also to solve the defects of the alignment of the transparent conductive layer and the pattern of the linear convex mesa.

In this invention, the first insulation layer is formed by the Prague reflective layer, the metal layer and the multilayer of oxide insulation, then the P type contact metal and the N type contact metal are plated, so that the photoelectric characteristic of the flip-chip can be measured in this step.

The description above is shown and described with several preferred embodiments of the disclosure, but as mentioned before, it should be understood the limitations of the disclosure are not disclosed in this form, it should not be regarded as the embodiment of the exclusion of the other, and can be used for a variety of other combinations, modifications, environments; and can be described in this article for ideas within the scope of change through the teaching or related fields of technology or knowledge. The changes and changes in the field of personnel in this field shall not be separated from the spirit and scope of the disclosure, and shall be within the scope of the protection required by the disclosure. 

What is claimed is:
 1. A manufacturing method of a flip-chip structure of III group semiconductor light emitting device, comprising the steps of: growing a substrate, a buffer layer, an N type nitride semiconductor layer, an active layer and a P type nitride semiconductor layer sequentially from bottom to top to form an epitaxial structure, wherein the top surface of the epitaxial structure is the top surface of the P type nitride semiconductor layer; depositing a transparent conductive layer on the top surface of the P type nitride semiconductor, defining a pattern of a linear convex mesa by using of a yellow light etching process, etching the transparent conductive layer, the P type nitride semiconductor layer and the active layer; exposing the N type nitride semiconductor layer; and shrinking the transparent conductive layer with etching solution; finally removing a photo resist to get the linear convex mesa whose top surface has the transparent conductive layer, wherein the linear convex mesa comprises a first top surface, a side surface and a second top surface, the first top surface and the second top surface individually connects with the side surface to form a L shape structure, the first top surface of the linear convex mesa being the top surface of the P type nitride semiconductor layer, the second top surface of the linear convex mesa being the top surface of the N type nitride semiconductor layer; in this step, individually forming the transparent conductive layer and the linear convex mesa, that is, not forming the transparent conductive layer and the linear convex mesa in the same etching step, but forming the transparent conductive layer at first and forming the linear convex mesa on the next, or forming the linear convex mesa at first and forming the transparent conductive layer on the next; defining an isolation groove with the yellow light etching process, then etching the N type nitride semiconductor layer and the buffer layer to expose the substrate, and finally removing the photo resist; or the isolation groove not be located in the flip-chip structure of the III group semiconductor light emitting device, or the isolation groove be located in any steps behind this step; depositing a first insulation layer structure which is formed by a Prague reflective layer, a metal layer and a multilayer of oxide insulation; wherein the Prague reflective layer is deposited at first, then a pattern on the metal layer is defined by a yellow light stripping process, the metal layer is deposited, and the photo resist is removed to get the metal layer by a stripping process, and the multilayer of oxide insulation is deposited, and then a connection pattern between a P type contact metal and the transparent conductive layer and a contact pattern between an N type contact metal and the second top surface of the linear convex mesa are defined by using of the yellow light etching process, then an connecting pattern between the multilayer of the oxide insulation and the Prague reflective layer is continuously etched, and finally the photo resist is removed to get the first insulation layer structure; defining a pattern of the P type contact metal and a pattern of the N type contact metal by the yellow light etching process, and depositing the P type contact metal and the N type contact metal in the mean time, and then the photo resist is removed with the stripping process to get the P type contact metal and the N type contact metal, therein, a bottom side of the P type contact metal is located on the surface of the transparent conductive layer and the first insulation layer structure, and a bottom side of the N type contact metal is located on the second top surface of the linear convex mesa and the surface of the first insulation layer structure; depositing a second insulation layer structure, wherein a pattern is defined by the yellow light etching process, the pattern is used for accessing the P type contact metal and the N type contact metal with an opening, then an opening pattern of the second insulation layer structure is etched, and finally the photo resist is removed; defining a pattern of a flip-chip P type electrode and a flip-chip N type electrode by the yellow light stripping process, wherein the flip-chip P type electrode and the flip-chip N type electrode is deposited, then the photo resist is removed by use of the stripping process to get a wafer; thinning, dicing, separating, measuring and sorting the wafer.
 2. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 1, wherein the first insulation layer structure is located on the first top surface, the side surface, the second top surface, the transparent conductive layer and the optional isolation groove.
 3. The manufacturing method a of flip-chip structure of III group semiconductor light emitting device of claim 1, wherein the structure of the Prague reflective layer comprises silicon dioxide and titanium dioxide, or is comprising of silicon dioxide and tantalic oxide, or is comprising of silicon dioxide and niobium oxide.
 4. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 3, wherein the thickness of the silicon dioxide is in a range of 30-1000 nm, the thickness of the titanium dioxide is in a range of 10-200 nm, the thickness of the tantalic oxide is in a range of 10-200 nm, and the thickness of the niobium oxide is in a range of 10-200 nm.
 5. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 3, wherein the Prague reflective layer is 3.5 pairs of silicon dioxide/titanium dioxide/silicon dioxide/titanium dioxide/silicon dioxide, or 3.5 pairs of silicon dioxide/tantalic oxide/silicon dioxide/tantalic oxide/silicon dioxide, or 3.5 pairs of silicon dioxide/niobium oxide/silicon dioxide/niobium oxide/silicon dioxide.
 6. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 1, wherein the first insulation layer structure is formed by the Prague reflective layer, the metal layer, the Prague reflective layer, the metal layer and the multilayer of the oxide insulation, a bottom side of the metal layer is located on the top surface of the Prague reflective layer of the first insulation layer structure, and/or is located in the multilayer of the oxide insulation layer of the first insulation layer structure.
 7. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 6, wherein the metal layer material is comprising of at least one of silver, aluminum, silver indium, platinum, nickel and titanium, therein a thickness of the silver, the aluminum, the indium and the platinum is respectively in a range of 50-500 nm, and a thickness of the nickel and the titanium is respectively in a range of 0.3-30 nm.
 8. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 6, wherein the multilayer of the oxide insulation layer is formed by at least two combinations of aluminum oxide, silicon dioxide, titanium dioxide, tantalic oxide, niobium oxide, silicon oxide and silicon nitride, a thickness of each layer of the multilayer of the oxide insulation is in a range of 30-200 nm.
 9. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 1, wherein the P type contact metal comprises a P type linear electrode and the P type connection metal; the bottom side of the P type linear electrode is located on the surface of the first insulation layer structure and the transparent conductive layer; the bottom side of the P type connection metal is located on the surface of first insulation layer structure; and the N type contact metal comprises an N type linear electrode and the N type connection metal, a bottom side of the N type linear electrode is located on the first insulation layer structure and the second top surface, a bottom side of the N type connection metal is located on the surface of the first insulation layer structure.
 10. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 1, wherein the structure of the P type contact metal and N type contact metal has the same structure which are a single metal layer or a multilayer of metal layer, and both sequentially comprise a first Ni layer, an Al layer, a second Ni layer, an Au layer and a third Ni layer from inner to outer, or sequentially comprise a Ti layer, an Al layer, the second Ni layer, an Au layer and the third Ni layer from inner to outer, or sequentially comprise the Ti layer, the Al layer and the third Ni layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer, the second Ni layer, a Pt layer, the Au layer and the third layer Ni from inner to outer, or sequentially comprise an Cr layer, the Pt layer, the Au layer and the third Ni layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer and the third Ni layer, or sequentially comprise an Rh layer, therein, a thickness of the Rh layer is in a range of 50-3000 nm, a thickness of the first Ni layer is in a range of 0.3-300 nm, a thickness of the Al layer is in a range of 50-300 nm, a thickness of the second Ni layer is in a range of 10-300 nm, a thickness of the Pt layer is in a range of 10-300 nm, a thickness of the Au layer is in a range of 10-3000 nm, a thickness of the third Ni layer is in a range of 0.3-300 nm.
 11. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 1, wherein the second insulation layer is disposed on the top surface of the first insulation layer, the top surface of the P type contact metal, and the top surface of the N type contact metal.
 12. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 11, wherein the second insulation layer structure is a multilayer of the oxide insulation, the multilayer of the oxide insulation is formed by at least two of the combinations of aluminum oxide, silicon dioxide, titanium dioxide, tantalic oxide, niobium oxide, silicon oxide and silicon nitride, a thickness of each layer of the multilayer of the oxide insulation is in a range of 30-2000 nm.
 13. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device of claim 1, wherein the bottom side of the flip-chip P type electrode is deposed on the surface of the P type contact metal and the second insulation layer, the bottom side of the flip-chip N type electrode is deposed on the surface of the N type contact metal and the second insulation layer structure.
 14. The manufacturing method of a flip-chip structure of III group semiconductor light emitting device as defined as claimed 13, wherein the flip-chip P type electrode and the flip-chip N type electrode has the same structure, both sequentially comprise a Ti layer and a second Ni layer and an Au layer from inner to outer, or sequentially comprise a middle Cr layer, a Pt layer, an Au layer, a second Ni layer a Pt layer, a second Ni layer and an AuSn layer from inner to outer, or sequentially comprise a first Ni layer and an Al layer, the second Ni layer and the Au layer from inner to outer, or sequentially comprise the middle Cr layer, the Pt layer and the Au layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer, the middle Cr layer and the second Ni layer and the Au layer from inner to outer, or sequentially comprise the first Ni layer, the Al layer, the second Ni layer, the Pt layer and the Au layer from inner to outer, therein a thickness of the first Ni layer is in a range of 0.4-3 nm, a thickness of the second Ni layer is in a range of 10-300 nm, a thickness of the Ti layer is in a range of 10-300 nm, a thickness of the Al layer is in a range of 50-300 nm, a thickness of the Au layer is in a range of 20-3000 nm, a thickness of the middle Cr layer is in a range of 10-300 nm, a thickness of the Pt layer is in a range of 10-300 nm, and a thickness of the AuSn layer is in a range of 1000-5000 nm. 